HB-YD114(Q)

1.6

50-55

(受强烈冲击后

After high impact)

高锰钢堆焊焊丝，受强烈冲击后，表面具有加工硬度的特点。

High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.

HB-YD115(Q)

1.6

50-55

(受强烈冲击后After high impact)

用于受严重冲击高锰钢堆焊，加工硬化效果显著。

Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.

HB-YD165(Q)

1.6

60-65

高硬度耐磨焊丝，适用于磨粒磨损表面堆焊

High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.

HB-YD172(Q)

1.6

≥40

用于堆焊齿轮、挖泥斗、矿山机械等磨损件

Applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery.

HB-YD207(Q)

1.6

≥50

用于堆焊推土机刀片，螺旋桨等磨损零件

Applied to repair surface of high wear parts, such as bulldozer blade and propeller.

HB-YD212(Q)

1.2/1.6

≥50

用于堆焊各种受磨损的机件表面，如齿轮、挖斗、矿山机械

Applied to repair surface of wear parts, such as gear mud bucket and mining machinery.

HB-YD256(Q)

1.6

HB≥170

高锰钢堆焊，适用于破碎机等受冲击磨损部位的堆焊

High-manganese steelhardfacing flux-cored Wires,it is applied to repair surface of high impact wear parts, such as Crusher.

HB-YD258(Q)

1.6

55-60

用于耐磨表面堆焊

Applied to repair surface of wear parts.

HB-YD265(Q)

1.6

60-65

高硬度耐磨焊丝，适用于磨粒磨损表面堆焊

High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.

HB-YD322(Q)

1.6

≥55

用于堆焊各种冲模及切削刃具，兼用于修复要求耐磨损性能较高之机械零件

Applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery.

HB-YD327A(Q)

1.6

≥55

专门用于模具堆焊，耐磨性能高于D322

Used tomouldsurfacing, wear resistance is better than D322.

HB-YD337(Q)

1.6

≥48

用于铸钢或锻钢上堆焊锻模

Applied to repairforging dieatcast steelorforging steel.