INCOFLUX ESS10 带极电渣焊剂设计与INCONEL 82／622／625和INCO-WELD C-276／686CPT带状焊接电极匹配使用。这种焊剂与这些合金电极匹配，可以用于碳钢的表面电渣堆焊。这种中性的烧结焊剂和电渣焊接过程使第二层堆焊金属的稀释率较低，其化学成分与电极的化学成分非常近似。尽管没有电磁操控作用，但熔融焊剂平滑致密的纹理和良好的润湿性仍可以保证堆焊层的平整。

储藏和干燥条件

焊剂密封在未开启的容器中可以无限期保存。如果焊剂暴露于潮湿环境中，可以在400^oF保温烘干2小时或500^oF保温烘干1小时后使用。

INCOFLUX ESS10 band electrode welding electrode was designed to match INCONEL 82/622/625 and INCO-WELD c-276/686cpt band welding electrode. The flux is matched with these alloy electrodes and can be used for surfacing of carbon steel surface. This neutral sintering flux and electroslag welding process makes the dilution rate of the second layer of welding metal low, and its chemical composition is very similar to the chemical composition of the electrode. Although there is no electromagnetic manipulation, the smooth and dense texture of melt flux and good wettability can guarantee the formation of the surfacing layer.

Welding parameters: applying DCEP current mode

Electrode size current/ampere voltage/v welding speed electrode dry extension flux layer thickness

0.5 x 60mm 1100-1300 23-24 6-7 in/min

In 150-175 - mm/min 0.75-1

0.75 1.5 in 19-25 mm

19-38 mm

0.5 x 30mm 600-700 23-246-7 in/min

In 150-175 - mm/min 0.75-1

0.75 1.5 in 19-25 mm

19-38 mm

Storage and drying conditions

The flux seals can be kept indefinitely in unopened containers. If the flux is exposed to humid environment, it can be used after an hour or so of heat preservation for 2 hours or 500oF heat preservation.

Flux particle size

Taylor's mesh: 12 by 68 eyes

packaging

88-pound (40Kg) polyethylene bag packagingINCOFLUX ESS10 带极电渣焊剂12×68目